Specification
- Product name: Modified PP Sheet Roll
- Brand: DESU
- Origin: Shanghai, China
- Width: 300-1400mm
- Thickness: 0.2-2.0mm
- Weight: 50-150kg/roll
- Shape: Roll/Sheet
- Color: Natural, Black, White, Color.
- Molding Process: Vacuum forming
Introduction
Modified polypropylene sheet is made of polypropylene as the main raw material, by adding various additives, by blending modification, through the special processing technology of twin-screw extrusion modification method extrusion granulation. It has the advantages of excellent processing performance and low price.
Properties
Item | Typical |
Density(23±0.5)℃ | 0.91g/cm3 |
Melt Flowing Index | 2.0g/10min |
Tensile strength at yield | 25MPa |
Elongation at break | 109% |
Flexural modulous | 1452MPa |
Bending strength | 26MPa |
Melting point | 167℃ |
HDShore hardness HD | 67 |
Heat distortion temp 0.45 M pa | 130℃ |
Coefficient of volume resistance | 1.1×1017Ω.㎝ |
Dielectric Constant | 2.3 |
Axial back shrinkage of loose tube | 0.35% |
Heat aging resistance of loose tube | No white, no crack |
Lateral pressure resistance of loose tube | 500N |